| خسارت: | CE 、 ISO9001 | Abrasion Resistance: | ≤ 0.8 cm3 |
|---|---|---|---|
| درخواست: | آستر کوره با دمای بالا | Package: | Wooden package |
| Customized: | yes | حوزه کاربرد: | خزدار |
| Origin: | Xinmi | Color: | White |
| Raw Material: | Insulation Clay | Transportation: | Shipping |
| احیاء خام: | درجه بالا | Thermalexpansion: | 4.5x10-6/K |
| Melting Point: | High | سرد، قدرت خرد کردن: | 100 مگاپاسکال |
| انبساط حرارتی: | ≤2.0×10-6/℃ | ||
| برجسته کردن: | High Temperature Fused Cast Bricks,AZS-36 Fused Cast Bricks,AZS-41 Fused Cast Bricks,AZS-36 Fused Cast Bricks,AZS-41 Fused Cast Bricks |
||
High Temperature Fused Cast Bricks Refractory Zirconia Corundum Brick AZS-41, AZS-36, AZS-33 for Glass Furnace
AZS bricks, also known as fused zirconia corundum bricks, are made by carefully selected zircon sand and industrial aluminum oxide powder in a 1:1 ratio, with a small amount of flux added, mixed evenly, melted at 1800~1900 ℃, and then cast into shape. Generally, zirconium corundum bricks can be divided into several grades according to the content of ZrO2, such as three grades of 33%, 36% and 41%. They have high melting point, good chemical stability, and strong corrosion resistance to acid and alkaline media, especially molten glass.
Features of AZS Brick
1.Casted by melting raw material in the mold, then cooling and solidification.
2.Strong glass corrosion resistance and high thermal shock stability.
3.Good wear-resistance,slag-resistance and alkali corrosion resistance.
4.High-purity raw material, barely no pollution.
5.Top quality, long service time.
Shapes and sizes: there are great variety of formats and shapes which are available for different forming and special machine processes.
Applications of AZS Brick
1.Sodium silicate furnace, ceramic frit furnace, glass furnace, etc..
2.Important parts of furnaces where chemical erosion is serious and temperature changes frequently.
3.Lining of glass furnace.
4.The chemical industrial, metallurgical furnaces.
Properties:
| chemical composition | AZS-33 | AZS-36 | AZS-41 |
| ZrO2 | ≥33 | ≥35 | ≥40 |
| SiO2 | ≤16.0 | ≤14 | ≤13.0 |
| Al2O3 | a little | a little | a little |
| Na2O | ≤1.5 | ≤1.6 | ≤1.3 |
| Fe2O3+TiO2 | ≤0.3 | ≤0.3 | ≤0.3 |
Physical Properties:
| bulk density(g/cm3): | 3.5-3.6 | 3.75 | 3.90 | |
| cold crushing Mpa | 350 | 350 | 350 | |
| thermal expansion coefficient (1000°C) | 0.80 | 0.80 | 0.80 | |
| exudation temp. of glass phase | 1400 | 1400 | 1400 | |
| corrocion resistance of glass melt(mm/24h) | 1.6 | 1.5 | 1.3 | |
| Density | PT QX | 3.40 | 3.45 | 3.55 |
| WS ZWS | 3.60 | 3.70 | 3.8 | |
Phase Composition(%):
| baddeleyite | 32 | 35 | 40 |
| glass phase | 21 | 18 | 17 |
| α- corundum | 47 | 47 | 43 |